PROPERTY |
TEST
METHOD |
RESULTS |
|
ACCELERATED WEATHERING |
ASTM
G-53 |
No
evidence of cracking, blistering or deterioration. Average
weight loss...0.95% |
| ABRASION RESISTANCE |
ASTM
C-501, Model 503 Tabor Abraser with CS-17 wheels, 1000
cycles, with a 1000 gram load |
weight
loss...0.3437 grams, wear loss...0.0008 inches |
| COEFFICIENT OF FRICTION |
ASTM
D-2047 |
Slip
resistant-(SCF) 0.63 |
| COMPRESSIVE STRENGTH |
ASTM
D-695-196,600 lbs. applied over 15.4 sq. in. |
12,766
PSI-product did not fracture or was otherwise affected |
| DIMENSIONAL STABILITY |
ASTM
D-756, using 5 cycles of 6 hours at 30 degree F followed
by 4 hours at 120 degree F |
No
dimensional changes, warpage or other effects noted on
product |
| FLAME SPREAD |
E84-81 |
Class
I |
| FUEL CONTRIBUTION |
E84-81 |
Class
I |
| SMOKE GENERATION |
ASTM
E662 |
Less
than 450 |
| FLAME RESISTANCE |
ASTM
E648 (radiant panel) |
Critical
radiant flux-0.50 W/cm2 |
| FLEXURAL STRENGTH 7 FLEXURAL MODULUS |
ASTM
D-790 |
Strength
1,139 PSI Modulus 698,340 PSI |
| HARDNESS |
BARCOL-ASTM
D-2583 Impressor-934-1 SHORE-ASTM D-2240 |
Aggregate
83.3 Matrix 64.4 |
| INDENTATION |
1
lb. steel ball applied with 200 lbs. of pressure for 30
minutes at 77 degree F |
Indentation...0.009
inches |
| SPECIFIC GRAVITY |
ASTM
D-792 |
2.20 |
| THERMAL SHOCK |
MIL-F-52505 |
No
evidence of peeling, cracking, crazing or deterioration |
| WATER ABSORPTION |
ASTM
D-570, Immersion in 75 degree F water for 24 hours after
conditioning for 24 hours at 212 degree F |
1.40% |
| WEIGHT |
300
Series - 3/16”
400 Series - 1/4”
600 Series - 3/8"
|
2.2
lbs. per sq. ft.
3.0
lbs. per sq. ft.
4.4 lbs. per sq. ft.
|